SAF 2507 stainless steel tube possesses good weldability and can be joined to itself or other materials by shielded metal arc welding (SMAW), gas tungsten arc welding (GTAW), plasma arc welding (PAW), flux cored wire (FCW), or submerged arc welding (SAW). 2507/P100 filler metal is suggested when welding SAF 2507 because it will produce the appropriate duplex weld structure.
Preheating of SAF 2507 is not necessary except to prevent condensation on cold metal. The interpass weld temperature should not exceed 300°F or the weld integrity can be adversely affected. The root should be shielded with argon or 90% N2/10% H2 purging gas for maximum corrosion resistance. The latter provides better corrosion resistance.
If welding is to be done on only one surface and post-weld cleaning is not possible, GTAW is suggested for root passes. GTAW or PAW should not be done without a filler metal unless post-weld cleanup is possible. A heat input of 5-38 kJ/in. should be used for SMAW or GTAW. A heat input of about 50kJ/in. can be used for SAW.
Back to 2507/S32750
General Properties
Application
Standards
Chemical Composition
Resistance to Corrosion
Physical Properties
Mechanical Properties
Welding
Processing
ASTM A789/A789M
ASTM A 790/A 790M
Duplex Stainless Steel Pipe
Austenitic-Ferritic Stainless Steel Pipe
Super-Duplex Stainless Steels and their characteristics
2507 S32750(1.4410) Duplex Steel
S32205 S31803(1.4462) Duplex Steel
S32304(1.4362) Duplex Steel
Compared with the ferritic stainless steel, duplex stainless steel vulnerable
Compared with the austenitic stainless steel, duplex stainless steel strengths and vulnerable
|