Alloy 310 |
| Density |
lbm/in3 |
g/cm3 |
| at 68°F (20°C) |
0.29
|
8.03 |
| Coefficient of Thermal Expansion |
(min/in)•°F |
(mm/m)•°K |
at 68 - 212°F
(20 - 100°C) |
8.8 |
15.9 |
at 68 - 932°F
(20 - 500°C) |
9.5 |
17.1 |
at 68 - 1832°F
(20 - 1000°C) |
10.5 |
18.9 |
| Electrical Resistivity |
mW•in |
mW•cm |
| at 68°F (20°C) |
30.7 |
78.0 |
| at 1200°F (648°C) |
-- |
-- |
| Thermal Conductivity |
Btu/hr•ft•°F |
W/m•K |
at 68 - 212°F
(20 - 100°C) |
8.0 |
13.8 |
at 68 - 932°F
(20 - 500°C) |
10.8 |
18.7 |
| Specific Heat |
Btu/lbm•°F |
J/kg•K |
at 32 - 212°F
(0 - 100°C) |
0.12 |
502 |
| Magnetic Permeability (annealed)1 |
|
| at 200H |
1.02 |
| Modulus of Elasticity (annealed)2 |
psi |
GPa |
| in tension (E) |
29 x 106
|
200 |
| in shear (G) |
11.2 x 106 |
77 |