These aluminium alloys ie., Non heat treatable, include commercially pure aluminium and the aluminium alloys including manganese or magnesium. These alloys can be fully or partly softened by annealing at 350 - 400 deg Celcius.
A small number of typical example aluminium allows are listed below.
| Grade. |
Cond'n |
Al |
Mg |
Mn |
Fe |
Si |
Cu |
Zn |
Cr |
Ti |
Rp.02 |
Rm |
E |
Notes |
| |
|
wt% |
wt% |
wt% |
wt% |
wt% |
wt% |
wt% |
wt% |
wt% |
MPa |
>MPa |
GPa |
|
| AW-1200 |
0 |
> 99% |
|
< 0.05 |
|
|
<=0,05 |
<=0,1 |
- |
<= 0,05 |
25 |
90 |
69 |
Packaging, foils, Miscellaneous |
| AW-1200 |
Hx4 |
> 99% |
|
< 0.05 |
|
|
<=0,05 |
<= 0,1 |
- |
<= 0,05 |
100 |
120 |
69 |
|
| AW-3003 |
0 |
Remain |
|
1,0-1,5 |
<= 0,7 |
<=0,6 |
0,05
-0,2 |
<= 0,10 |
- |
- |
50 |
110 |
69,5 |
Building Industry, Roofing etc |
| AW-3003 |
Hx6 |
Remain |
|
1,0 - 1,5 |
<= 0,7 |
<=0,6 |
0,05
-0,2 |
<= 0,10 |
- |
- |
165 |
180 |
69,5 |
|
| AW-5005 |
0 |
Remain |
0,5
-1,1 |
< = 0,2 |
<= 0,7 |
<= 0,2 |
<= 0,2 |
<= 0,25 |
<= 0,10 |
- |
45 |
120 |
69,5 |
Building Industry, Roofing etc |
| AW-5005 |
Hx6 |
Remain |
0,5
-1,1 |
<= 0,2 |
<= 0,7 |
<= 0,2 |
<= 0,2 |
<= 0,25 |
<= 0,10 |
- |
165 |
180 |
69,5 |
|
| AW-5086 |
0 |
Remain |
3,45
-4,5 |
0,2-0,7 |
<= 0,5 |
<= 0,4 |
<= 0,1 |
<= 0,25 |
0,05-
0,25 |
<= 0,15 |
130 |
275 |
71 |
Structures equipment, Piping, tanks |
| AW-5086 |
Hx6 |
Remain |
3,45
-4,5 |
0,2-0,7 |
<= 0,5 |
<= 0,4 |
<= 0,1 |
<= 0,25 |
0,05 - 0,25 |
<= 0,15 |
280 |
345 |
71 |
|